Periodically Poled Stoichiometric Lithium Tantalate

Product Description

Periodically Poled Stoichiometric Lithium Tantalate chips offer a cost effective method for visible and mid-infrared frequency generation. A multi-step lithographic and electric field poling process effects a permanent change in the non-linear properties of Lithium Tantalate. Using quasi-phase matching, with a selection of periods, crystal widths and lengths, PPSLT offers users an alternative to dedicated frequency conversion crystals.

Applications

  • RGB laser generation
  • IR/Mid-IR laser generation
  • Visible Light Generation
  • 1st order or higher order wavelength conversion
  • Remote Sensing

 

Features

  • Difference and Sum Frequency Generation
  • Broad-Range, Precise Frequency Conversion
  • High Conversion Efficiency from Low Peak-Power Laser Sources
  • Offers Pathway to Compact Designs for Portable Systems
  • Single and Multiple Gratings Available

 

Specifications  
Chip Thickness (standard) 0.5; 1; 2; 3 mm
Chip Width (standard) 5mm and 10mm (custom up to 40mm)
Chip Length (standard) 10, 20, 30, 40, 50mm (custom up to 60mm)
Single Grating Periods Many periods available in the range 4 to 100+ µm
(plus custom periods)
Multiple Grating Periods Many multiple grating designs available
Fan-out QPM To customer specifications
Type I and Type II Phase Matching To customer specifications
AR Optical Coatings double band, triple band, broadband
End Surfaces Optically polished to target specifications
Parallelism (arc min) < 10 (custom < 1)
Flatness λ/10
Scratch/Dig 10/5
   
Material Propery LiTaO3 (Lithium Tantalate)
Transparency Range 280nm - 5500nm
Refractive Index 2.2
Nonlinearity d31 = 0.85pm/V
d33 = -13.8pm/V
Surface Damage Threshold for 10ns (J/cm2) > 10
Phasematching Schemes QPM
* The above figures are based on wavelength at 1064nm and software "SNLO"